PRODUCT DESCRIPTION

Tasir®-Epoth is a thixotropic, 3-component patching and repair mortar, based on a combination of epoxy resins and special fillers, designed for use at temperatures between +10 °C and +30 °C.


3-component-thixotropic-epoxy-patching-mortar30279663004


USES

As a repair and bonding mortar for:

▪ Concrete elements

▪ Hard natural stone

▪ Ceramics, fibre cement

▪ Mortar, Bricks, Masonry

▪ Steel, Iron, Aluminium

▪ Wood

▪ Polyester, Epoxy

▪ Glass

As a repair mortar:

▪ Filling of cavities and voids

▪ Vertical and overhead use

▪ Corners and edges

As an abrasion and impact resistant wearing course:

▪ Joint filling and crack sealing

▪ Joint and crack arris / edge repair

 

CHARACTERISTICS / ADVANTAGES

Tasir®-Epoth has the following advantages:

▪ Easy to mix and apply

▪ Very good adhesion to most construction materials

▪ High strength

▪ Thixotropic: Non-sag in vertical and overhead applic- ations

▪ Hardens without shrinkage

▪ Different coloured components (for mixing control)

▪ No primer needed

▪ High initial and ultimate mechanical strength

▪ Good abrasion resistance

▪ Good chemical resistance


APPROVALS / STANDARDS

Mortar for structural and non-structural repair, tested according to EN 1504-3, provided with the CE-mark

 

PRODUCT INFORMATION

11.jpg

22.jpg


TECHNICAL INFORMATION

33.jpg

44.jpg


APPLICATION INFORMATION


APPLICATION INSTRUCTIONS

SUBSTRATE QUALITY

Mortar and concrete must be older than 28 days (de- pends on minimal requirement of strengths).

Verify the substrate strength (concrete, masonry, nat- ural stone).

The substrate surface (all types) must be clean, dry or mat damp (no standing water) and free from contam- inants such as dirt, oil, grease, existing surface treat- ments and coatings etc.

Steel substrates must be de-rusted similar to Sa 2.5 The substrate must be sound and all loose particles must be removed.


SUBSTRATE PREPARATION

Concrete, mortar, stone, bricks:

Substrates must be sound, dry or mat damp (no stand- ing water), clean and free from laitance, ice, grease, oils, old surface treatments or coatings and all loose or friable particles must be removed to achieve a lait- ance and contaminant free, open textured surface.

Steel:

Must be cleaned and prepared thoroughly to an ac- ceptable quality i.e. by blast-cleaning and vacuum. Avoid dew point conditions.

 

MIXING

Pre-batched units:

Mix components A+B together for at least 3 minutes with a mixing spindle attached to a slow speed electric drill (max. 300 rpm) until the material becomes smooth in consistency and a uniform grey colour. Then add part C and continue until mixture is homogeneous. Avoid aeration while mixing. Then, pour the whole mix into a clean container and stir again for approx. 1 more minute at low speed to keep air entrapment at a min- imum. Mix only that quantity which can be used with- in its pot life.


APPLICATION METHOD / TOOLS

Brush the adhesive well into the substrate. Tasir®-CP be used as primer to improve the bond.

When using a thin layer adhesive, apply the mixed ad- hesive to the prepared surface with a spatula, trowel, notched trowel, (or with hands protected by gloves). When applying as a repair mortar, use some form- work.

When using for bonding metal profiles onto vertical surfaces ,support and press uniformly using props for at least 12 hours, depending on the thickness applied (not more than 5 mm) and the room temperature.

Once hardened check the adhesion by tapping with a hammer.


CLEANING OF TOOLS

Clean all tools and application equipment with Tasir® Cleaner immediately after use. Hardened / cured material can only be removed mechanically.


LIMITATIONS

Tasir® resins are formulated to have low creep un- der permanent loading. However due to the creep be- haviour of all polymer materials under load, the long term structural design load must account for creep.

Generally the long term structural design load must be lower than 20–25 % of the failure load.

 

VALUE BASE

All technical data stated in this Product Data Sheet are based on laboratory tests. Actual measured data may vary due to circumstances beyond our control.


LOCAL RESTRICTIONS

Please note that as a result of specific local regula- tions the performance of this product may vary from country to country. Please consult the local Product Data Sheet for the exact description of the application fields.


ECOLOGY, HEALTH AND SAFETY

For information and advice on the safe handling, stor- age and disposal of chemical products, users shall refer to the most recent Safety Data Sheet (SDS) containing physical, ecological, toxicological and other safety-re- lated data.

 

LEGAL NOTES

The information, and, in particular, the recommendations relating to the application and end-use of TASIR products, are given in good faith based on TASIR's current knowledge and experience of the products when properly stored, handled and applied under normal conditions in accordance with TASIR’s recommendations. In practice, the differences in materials, substrates and actual site conditions are such that no warranty in respect of merchantability or of fitness for a particular purpose, nor any liability arising out of any legal relationship whatsoever, can be inferred either from this information, or from any written recommendations, or from any other advice offered. The user of the product must test the product's suitability for the intended application and purpose. TASIR reserves the right to change the properties of its products. The proprietary rights of third parties must be observed. All orders are accepted subject to our current terms of sale and delivery. Users must always refer to the most recent issue of the local Product Data Sheet for the product concerned, copies of which will be supplied on request.


Tasir Construction Material&Technology Corporate Headquarters

Tianda Block, Jianggan District, Hangzhou City, Zhejiang Province, China

Tel: +86-571-28119206 

Fax: +86-571-28197878

groutmaterial.com


Specifications Subject to Change.

For most current version of datasheet, go to groutmaterial.com

© 2018Tasir Construction Material&TechnologyCp.,Ltd | 08-21-2018 Rev. H | China Owned & Operated


Hot Tags: 3-component thixotropic epoxy patching mortar, China, suppliers, manufacturers, cheap, made in China
Related Products
Copyright © Zhejiang Taizheng Construction Material Co.,Ltd All Rights Reserved.